Deposition and characterization of duplex treated coating system applied on hot work steel AISI H13

Vista sencilla de ítem
dc.citation.journalTitleRevista Latinoamericana De Metalurgia Y Materiales
dc.contributor.authorGaitan, G.B.
dc.contributor.authorBotero, M.G.
dc.contributor.authorFranco, M.A.
dc.contributor.departmentUniversidad EAFIT. Departamento de Ciencias Básicas
dc.contributor.researchgroupElectromagnetismo Aplicado (Gema)spa
dc.date.accessioned2021-03-23T21:39:32Z
dc.date.available2021-03-23T21:39:32Z
dc.date.issued2012-01-01
dc.description.abstractAISI H13 steel is widely used for extrusion moulds and other hot work tools fabrication, due to its high toughness, strength and hardness around 56 HRC (Rockwell C). However, this steel possesses a relatively low wear resistance, which reduces its life time under high loading conditions. The aim of this work was to enhance the wear resistance of the steel H13 using the following surface treatments: austenitizing + quenching + tempering (further called "tempering"), tempering and bath nitriding, tempering and coated with chromium nitride (CrN), tempering + bath nitriding + coated with CrN (further called "Duplex coating"). The properties of the treated samples were compared with each other in dependence of the made surface treatment. The coatings were deposited using the r.f. balanced magnetron sputtering deposition technique. The total thickness of the coatings was maintained at 5 µm, while the thickness of the nitrided zone was approximately 140 µm. The microstructure and the crystalline phase composition were investigated by Scanning Electron Microscopy (SEM) and X-ray diffraction (XRD) technique, respectively. The hardness and the adhesion of the coatings were determined by micro indentation measurements and the Rockwell indentation test, respectively. The wear resistance of the coatings was evaluated using ball on disc tests. The duplex treated samples presented a hardness three order of magnitude higher and showed a wear rate six times smaller than those samples only tempered. © 2012 Universidad Simón Bolívar.eng
dc.identifierhttps://eafit.fundanetsuite.com/Publicaciones/ProdCientif/PublicacionFrw.aspx?id=2054
dc.identifier.issn2556952spa
dc.identifier.otherSCOPUS;2-s2.0-84858112823
dc.identifier.urihttp://hdl.handle.net/10784/27157
dc.language.isoengeng
dc.publisherUniversidad Simon Bolivar
dc.relation.urihttps://www.scopus.com/inward/record.uri?eid=2-s2.0-84858112823&partnerID=40&md5=32693dc20703272d68d4873570391897
dc.rightsUniversidad Simon Bolivar
dc.sourceRevista Latinoamericana De Metalurgia Y Materiales
dc.subject.keywordChromium nitrideseng
dc.subject.keywordDuplex treatmenteng
dc.subject.keywordMagnetron sputteringeng
dc.subject.keywordWear resistanceeng
dc.titleDeposition and characterization of duplex treated coating system applied on hot work steel AISI H13eng
dc.typearticleeng
dc.typeinfo:eu-repo/semantics/articleeng
dc.typeinfo:eu-repo/semantics/publishedVersioneng
dc.typepublishedVersioneng
dc.type.localArtículospa

Archivos

Colecciones

Artículos (Gema)