Examinando por Materia "Puncture"

Mostrando 1 - 2 de 2
  • No hay miniatura disponible
    Ítem
    Designed for resistance to puncture: The dynamic response of fish scales
    (ELSEVIER SCIENCE BV, 2019-01-01) Ghods S.; Murcia S.; Ossa E.A.; Arola D.; Ghods S.; Murcia S.; Ossa E.A.; Arola D.; Universidad EAFIT. Departamento de Ingeniería de Producción; Materiales de Ingeniería
    Natural dermal armors are serving as a source of inspiration in the pursuit of “next-generation” structural materials. Although the dynamic strain response of these materials is arguably the most relevant to their performance as armors, limited work has been performed in this area. Here, uniaxial tension and transverse puncture tests were performed on specimens obtained from the scales of Asian carp over strain rates spanning seven decades, from 10-4 to 103 s-1. The importance of anatomical variations was explored by comparing the performance of scales from the head, middle and tail regions. In both loading orientations, the scales exhibited a significant increase in the resistance to failure with loading rate. The rate sensitivity was substantially higher for transverse loading than for in-plane tension, with average strain rate sensitivity exponents for measures of the toughness of 0.35 and 0.08, respectively. Spatial variations in the properties were largest in the puncture responses, and scales from the head region exhibited the greatest resistance to puncture overall. The results suggest that the layered microstructure of fish scales is most effective at resisting puncture, rather than in-plane tension, and its effectiveness increases with rate of loading. X-ray microCT showed that delamination of plies in the internal elasmodine and stretching of the fibrils were key mechanisms of energy dissipation in response to puncture loading. Understanding contributions from the microstructure to this behavior could guide the development of flexible engineered laminates for penetration resistance and other related applications. © 2018 Elsevier Ltd
  • No hay miniatura disponible
    Ítem
    Interfibril hydrogen bonding improves the strain-rate response of natural armour
    (Royal Society Publishing, 2019-01-01) Arola D.; Ghods S.; Son C.; Murcia S.; Ossa E.A.; Arola D.; Ghods S.; Son C.; Murcia S.; Ossa E.A.; Universidad EAFIT. Departamento de Ingeniería de Producción; Materiales de Ingeniería
    Fish scales are laminated composites that consist of plies of unidirectional collagen fibrils with twisted-plywood stacking arrangement. Owing to their composition, the toughness of scales is dependent on the intermolecular bonding within and between the collagen fibrils. Adjusting the extent of this bonding with an appropriate stimulus has implications for the design of next-generation bioinspired flexible armours. In this investigation, scales were exposed to environments of water or a polar solvent (i.e. ethanol) to influence the extent of intermolecular bonding, and their mechanical behaviour was evaluated in uniaxial tension and transverse puncture. Results showed that the resistance to failure of the scales increased with loading rate in both tension and puncture and that the polar solvent treatment increased both the strength and toughness through interpeptide bonding; the largest increase occurred in the puncture resistance of scales from the tail region (a factor of nearly 7). The increase in strength and damage tolerance with stronger intermolecular bonding is uncommon for structural materials and is a unique characteristic of the low mineral content. Scales from regions of the body with higher mineral content underwent less strengthening, which is most likely the result of interference posed by the mineral crystals to intermolecular bonding. Overall, the results showed that flexible bioinspired composite materials for puncture resistance should enrol constituents and complementary processing that capitalize on interfibril bonds. © 2019 The Author(s) Published by the Royal Society. All rights reserved.