    Effect of chemical composition and microstructure on the mechanical behavior of fish scales from Megalops Atlanticus
    (ELSEVIER SCIENCE BV, 2016-03-01) Gil-Duran, S.; Arola, D.; Ossa, E.A.; Gil-Duran, S.; Arola, D.; Ossa, E.A.; Universidad EAFIT. Departamento de Ingeniería de Producción; Materiales de Ingeniería
    This paper presents an experimental study of the composition, microstructure and mechanical behavior of scales from the Megalops Atlanticus (Atlantic tarpon). The microstructure and composition were evaluated by Scanning Electron Microscopy (SEM) and RAMAN spectroscopy, respectively. The mechanical properties were evaluated in uniaxial tension as a function of position along the length of the fish (head, mid-length and tail). Results showed that the scales are composed of collagen and hydroxyapatite, and these constituents are distributed within three well-defined layers from the bottom to the top of the scale. The proportion of these layers with respect to the total scale thickness varies radially. The collagen fibers are arranged in plies with different orientations and with preferred orientation in the longitudinal direction of the fish. Results from the tensile tests showed that scales from Megalops Atlanticus exhibit variations in the elastic modulus as a function of body position. Additional testing performed with and without the highly mineralized top layers of the scale revealed that the mechanical behavior is anisotropic and that the highest strength was exhibited along the fish length. Furthermore, removing the top mineralized layers resulted in an increase in the tensile strength of the scale. © 2015 Elsevier Ltd.
  • No hay miniatura disponible
    Ítem
    Indentation damage and crack repair in human enamel.
    (ELSEVIER SCIENCE BV, 2013-05-01) Rivera C; Arola D; Ossa A; Rivera C; Arola D; Ossa A; Universidad EAFIT. Departamento de Ingeniería de Producción; Materiales de Ingeniería
    Tooth enamel is the hardest and most highly mineralized tissue in the human body. While there have been a number of studies aimed at understanding the hardness and crack growth resistance behavior of this tissue, no study has evaluated if cracks in this tissue undergo repair. In this investigation the crack repair characteristics of young human enamel were evaluated as a function of patient gender and as a function of the distance from the Dentin Enamel Junction (DEJ). Cracks were introduced via microindentation along the prism direction and evaluated as a function of time after the indentation. Microscopic observations indicated that the repair of cracks began immediately after crack initiation and reaches saturation after approximately 48 h. During this process he crack length decreased up to 10% of the initial length, and the largest degree of reduction occurred in the deep enamel, nearest the DEJ. In addition, it was found that the degree of repair was significantly greater in the enamel of female patients.